MPC的凝结时间.docx

《MPC的凝结时间.docx》由会员分享，可在线阅读，更多相关《MPC的凝结时间.docx（2页珍藏版）》请在第壹文秘上搜索。

1、1、本周进行了MPC大批量试验，室温为2223C,正交试验数据如下表:素组端、P/M水胶比硼砂(%)凝结时间3h强度(MPa)抗折抗压11/30.15212,106.6058.4621/30.1648,406.7749.7031/30.17610,107.9038.3741/30.188950“5.1330.1551/40.154810“7.7041.0261/40.162IOz306.3728.8971/40.178920,6.2724.9081/40.1867,30“6.0026.7691/50.156730”4.6820.25101/50.16810,204.3217.78111/50J

2、7216z504.0521.58121/50.184IOz053.6514.22131/60.15812,052.9511.10141/60.16610062.8011.27151/60.17411,502.4210.69161/60.18217,402.3512.822、正交试验数据极差分析极差分析表7素组处、P/M水胶比硼砂(%)空列空列抗压强度11/30.1521158.4621/30.1642249.7031/30.1763338.3741/30.1884430.1551/40.1543441.0261/40.1624328.8971/40.1781224.9081/40.186212

3、6.7691/50.1564220.25101/50.1683117.78111/50.1722421.58121/50.1841314.22131/60.1582311.10141/60.1661411.27151/60.1744110.69161/60.1823212.82Ki176.68130.83121.75108.85113.69K2121.57107.64115.63109.14107.67K373.8395.5496.65109.9992.58K445.8883.9583.9389.98104.02极差R130.8046.8837.8220.0121.11（1）极差分析法的因素主

4、次顺序：P/M水胶比一硼砂；（2）极差分析法的优选方案：PM=13,水胶比=0.15,硼砂掺量2机3、前两周做了镁水泥隧道防火涂料试块，由于新买的石棉板吸水比以前厉害，两天后石棉板表面还是湿的，导致试块强度很低，进行粘结强度测试时接触面脱落，无法测试。因此，以后的操作过程中石棉板表面只需稍微擦湿即可。二、试验计划我一直觉得用MPC的凝结时间和抗压强度指标来选择隧道防火涂料中水泥的配方不是很有说服力，这几天看了一些文献，认为采用水泥净浆粘结强度作为试验指标更合理。测试MPC与普通硅酸盐水泥砂浆之间的粘结强度采用间接的方法，用抗折强度表示。普通硅酸盐水泥砂浆试件配合比为m（水泥）：m（砂）：m（水）=1.0：3.0:0.5,按GB/T176711999水泥胶砂强度检验方法（ISo法）成型养护28d备用。用切割机将普通硅酸盐水泥砂浆试块从中间切开，用打磨机将新切断面磨平。将处理后试件浸泡于水中Id后取出，用湿抹布将试件表面水份擦干，使试件处于饱和面干状态。将切断后的基体试件成对固定在试模中，切断面留Iomm的间隔。将搅拌好的MPC净浆浇注于所留基体试块的间隙中，用捣棒捣实和刮刀刮平振实。成型好的试件1h后脱模，测其3h抗折强度。三1粘结强度试验方法示意